负载氢氧化镧的膨胀石墨除磷剂的制备、性能及再生

doi:10.3969/j.issn.1007-2861.2015.02.017

摘要/Abstract

摘要：

采用浸渍法成功制备了负载LaOH 的膨胀石墨除磷剂(expanded graphite-LaOH, EG-LaOH), 探讨了制备过程中的最优工艺条件, 考察了初始磷浓度、投加量、干扰离子和再生对吸附剂除磷性能的影响. 制备EG-LaOH 的最优工艺条件如下: 镧浓度为0.10 mol/L, 浸渍时间为40 min. 随着初始磷浓度的增加, EG-LaOH 的除磷吸附容量逐渐增大, 继而保持恒定. 随着吸附剂投加量的增加, 其除磷吸附容量逐渐降低. 溶液中F⁻, Cl⁻的存在对该吸附剂的除磷效果有一定的干扰. 该吸附剂在25 和90 ℃下再生一次后, 其除磷吸附容量分别为9.48 和14.40 mg/g.

关键词: 镧, 膨胀石墨, 再生, 除磷

Abstract:

Expanded graphite-LaOH (EG-LaOH) was fabricated successfully using an immersion method. The best synthesis conditions were studied. Influences of initial phosphate concentration, interfering anions and dosage were investigated as well. The best condition of EG-LaOH preparation was La concentration of 0.10 mol/L and immersion time of 40 min. Removal capacity of EG-LaOH was gradually improved and then kept unchanged with the increase of phosphate concentration but decreased with the rise of dosage. F⁻ and Cl⁻ had only limited impact on phosphorus removal of EG-LaOH. After the first recovery under the condition of 25 and 90 ℃, removal capacities of EG-LaOH could still reach 9.48 and 14.40 mg/g, respectively.

Key words: lanthanum , expanded graphite (EG) , recovery, phosphate adsorption

苏阳, 靳苏皖, 张玲. 负载氢氧化镧的膨胀石墨除磷剂的制备、性能及再生[J]. 上海大学学报(自然科学版), 2016, 22(6): 776-783.

SU Yang, JIN Suwan, ZHANG Ling. Preparation, performance and recovery of expanded graphite loaded with lanthanum hydroxide[J]. Journal of Shanghai University（Natural Science Edition）, 2016, 22(6): 776-783.

[1] Li T, Jia Z X. Analysis on the current situation of lake pollution and remediation in China [J]. Sci-Tech Information Development & Economy, 2010, 20(18): 181-183.
[2] Sengupta A K, Zhao D Y. Ultimate removal of phosphate from wastewater using a new class of polymeric ion exchange [J]. Water Research, 1998, 32: 1613-1625.
[3] Sunil K R, Loren G, Gunawan G, et al. A comprehensive review of phosphorus removal technologies and processes [J]. Journal of Macromolecular Science, Part A: Pure and Applied Chemistry, 2014, 51: 538-545.
[4] Lee S H, Yeon K H, Park H, et al. Zirconium mesostructures immobilized in calcium alginate for phosphate removal [J]. Korean J Chem Eng, 2008, 25: 1040-1046.
[5] Lin J W, Liu Y, Zhan Y H. Adsorption and desorption of phosphate on CPB modified zeolite [J]. Chinese Journal of Environmental Engineering, 2010, 4(3): 575-580.
[6] Xing Z, Chen Y C, Xiong B L. Static adsorption characteristics and removal efficiency of phosphate in biogas slurry by different zeolite substrates [J]. Chinese Journal of Environmental Engineering, 2013, 7(2): 494-500.
[7] Kostura B, Kulveitova H, Lesko J. Blast furnace slags as sorbents of phosphate from water solutions [J]. Water Research, 2005, 39(9): 1795-1802.
[8] Lu S G, Bai S Q, Shan H D. Mechanisms of phosphate removal from aqueous solution by blast furnace slag and steel furnace slag [J]. Journal of Zhejiang University: Science A, 2008, 9(1): 125-132.
[9] Huang W W, Wang S B, Zhu Z H, et al. Phosphate removal from wastewater using red mud [J]. Journal of Hazardous Materials, 2008, 158(1): 35-42.
[10] Chen J, Luan Z K. Enhancing phosphate removal by coagulation using polyelectrolytes and red mud [J]. Fresenius Environmental Bulletin, 2010, 19(10): 2200-2204.
[11] Dimirkou A, Ioannou A, Doula M. Preparation, characterization and sorption for phosphates of hematite, bentonite and bentonite-hematite systems [J]. Advanced in Colloid and Interface Science, 2002, 97(1/2/3): 37-61.

[12] Xu J H, Li Y M, Xie Y F. Adsorption of hydroxy-metal pillared bentonite to phosphate [J]. Non-metallic Mines, 2006, 29(5): 44-46.
[13] Li H, Ru J Y, Yin W, et al. Removal of phosphate from polluted water by lanthanum doped vesuvianite [J]. Journal of Hazardous Materials, 2009, 168(1): 326-330.
[14] Masto R E, Mahato M, Selvi V A. et al. The effect of fly ash application on phosphorus availability in an acid soil [J]. Energy Sources, Part A: Recovery, Utilization, and Environmental Effects, 2013, 25: 2274-2283.
[15] Cheung K C, Venkitachalam T H. Improving phosphate removal of sand infiltration system using alkaline fly ash [J]. Chemosphere, 2000, 41: 243-249.
[16] Ugurlu A, Salman B. Phosphorus removal by fly ash [J]. Environment International, 1998, 24(8): 911-918.
[17] Ayoub G M, Koopman B, Pandya N. Iron and aluminum hydroxy (oxide) coated filter media for low-concentration phosphorus removal [J]. Water Environ Res, 2001, 73: 478.
[18] Yan Y P, Liu J R, Li W, et al. Sorption and desorption characteristics of organic phosphates of different structures on aluminum (oxyhydr) oxides [J]. European Journal of Soil Science, 2014, 65: 308-317.
[19] Hu H Q, Li X Y, He J Z, et al. Secondary adsorption of phosphate on aluminum oxides surfaces as influenced by several organic acids [J]. Journal of Plant, 2004, 27: 637-649.
[20] Jiang C, Jia L Y, He Y L, et al. Adsorption removal of phosphorus from aqueous solution using sponge iron and zeolite [J]. Journal of Colloid and Interface Science, 2013, 402: 246-252.
[21] Shi Z L, Liu F, Yao S H. Adsorptive removal of phosphate from aqueous solutions using activated carbon loaded with Fe(Ⅲ) oxide [J]. New Carbon Materials, 2011, 26(4): 299-306.
[22] Biswas B K, Inoue K, Ghimire K N, et al. Removal and recovery of phosphorus from water by means of adsorption onto orange waste gel loaded with zirconium [J]. Bioresource Technology, 2008, 99(18): 8685-8690.
[23] Zhang Q R, Du Q, Jiao T F, et al. Selective removal of phosphate in waters using a novel of cation adsorbent: zirconium phosphate(ZrP) behavior and mechanism [J]. Chemical Engineering Journal, 2013, 221: 315-321.
[24] Xie J, Wang Z, Lu S Y, et al. Removal and recovery of phosphate from water by lanthanum hydroxide materials [J]. Chemical Engineering Journal, 2014, 254: 163-170.
[25] Reitzel K, Andersen F, Egemose S, et al. Phosphate adsorption by lanthanum modified bentonite clay in fresh and brackish water [J]. Water Research, 2013, 47: 2787-2796.
[26] Kuroki V, Bosco G E, Pedro S. et al. Use of a La(Ⅲ)-modified bentonite for effective phosphate removal from aqueous media [J]. Journal of Hazardous Materials, 2014, 274: 124-131.
[27] Lurling M, Waajen G, Oosterhout F. Humic substances interfere with phosphate removal by lanthanum modified clay in controlling eutrophication [J]. Water Research, 2014, 54: 78-88.
[28] Zhang L, Wan L H, Chang N, et al. Removal of phosphate from water by activated carbon fiber loaded with lanthanum oxide [J]. Journal of Hazardous Materials, 2011, 190: 848-855.
[29] Zhang L, Zhou Q, Liu J Y, et al. Phosphate adsorption on lanthanum hydroxide-doped activated carbon fiber [J]. Chemical Engineering Journal, 2012, 185: 160-167.

[30] Liu J Y, Zhou Q, Chen J H, et al. Phosphate adsorption on hydroxyl-iron-lanthanum doped activated carbon fiber [J]. Chemical Engineering Journal, 2013, 215: 859-867.
[31] Zhan C C, Yan P, Cao X H, et al. Treatment of methyl wastewater by synergistic catalytic oxidation precess with microwave-H₂O₂-expanded graphite [J]. Environmental Protection of Chemical Industry, 2011, 31(5): 397-401.
[32] American Public Health Association, American Water Works Association, Water Environment Federation. Standard methods for the examination of water and wastewater [S]. 20th ed. Washington DC: APH Association, 1998.
[33] Golikand A N, Aghazadeh M, Ghaemi M, et al. A novel lanthanum hydroxide nanostructure prepared by cathodic electrodeposition [J]. Mater Letter, 2011, 65: 1466-1468.
[34] Soejoko D S, Tjia M O. Infrared spectroscopy and X-ray diffraction study on the morphological variations of carbonate and phosphate compounds in giant prawn (Macrobrachium
rosenbergii) skeletons during its moulting period [J]. J Mater Sci, 2003, 38: 2087-2093.
[35] Li L, Jiang W, Pan H, et al. Improved luminescence of lanthanide (Ⅲ)-doped nanophosphors by linear aggregation [J]. J Phys Chem C, 2007, 111: 4111-4115.

负载氢氧化镧的膨胀石墨除磷剂的制备、性能及再生

Preparation, performance and recovery of expanded graphite loaded with lanthanum hydroxide

PDF

可视化

被引次数

摘要/Abstract

引用本文

使用本文

相关文章 15

编辑推荐

Metrics

本文评价

[1]	陆佳桢, 徐陈, 郑瑜, 尚奕辰, 李颖. Ln³⁺功能化碳点双发射荧光凝胶球的制备及其防伪应用[J]. 上海大学学报(自然科学版), 2025, 31(3): 444-453.
[2]	岳美如, 胡佳俊, 高旻天, 李继香, 刘楠. 生物炭释出物的效应及其缓解策略与应用[J]. 上海大学学报(自然科学版), 2023, 29(6): 1003-1021.
[3]	程金瑾, 金鑫, 汪圳, 娄洁. 北京 MSM 人群 HIV 传播的贝叶斯推断[J]. 上海大学学报(自然科学版), 2021, 27(6): 1138-1143.
[4]	靳苏皖, 牛维亚, 张玲, 毛纤勇. 镧氧化物/膨胀石墨复合吸附剂的制备、除磷性能及机理[J]. 上海大学学报(自然科学版), 2021, 27(4): 686-695.
[5]	梁小娇, 阮玉华, 娄洁. 男男性行为人群中 HIV/AIDS 行为干预的动力学模型[J]. 上海大学学报(自然科学版), 2019, 25(6): 898-907.
[6]	黄颖, 娄洁. HIV在人体免疫网络中传播的动力学研究[J]. 上海大学学报(自然科学版), 2017, 23(6): 920-.
[7]	朱浩1, 丁胜光1, 黄海涛1, 许嘉鸿2, 仲崇俊1. 新生大鼠心脏再生模型的改良及评价模式[J]. 上海大学学报(自然科学版), 2017, 23(3): 387-394.
[8]	高峰1,2, 陈静海1,2. 非编码RNA调控心脏重构与再生[J]. 上海大学学报(自然科学版), 2016, 22(3): 302-309.
[9]	贝毅桦, 肖俊杰. 运动诱导心脏再生: 治疗心血管疾病的新途径[J]. 上海大学学报(自然科学版), 2016, 22(3): 293-301.
[10]	胡士军1,2, 虞游1,2, 方星1,2, 雷伟1,2, 赵振奥1,2. 诱导多能干细胞与心脏再生[J]. 上海大学学报(自然科学版), 2016, 22(3): 285-292.
[11]	龚惠, 陈志丹, 邹云增. 干细胞与心肌再生[J]. 上海大学学报(自然科学版), 2016, 22(3): 280-284.
[12]	肖俊杰. 心脏重构与再生: 心血管研究热点聚焦[J]. 上海大学学报(自然科学版), 2016, 22(3): 261-264.
[13]	邓一飞, 戴佳莺, 吴雯君, 张文举, 陈沁, 邓志瑞. 镉对匍匐翦股颖成熟胚愈伤组织诱导及再生的影响[J]. 上海大学学报(自然科学版), 2013, 19(6): 636-640.
[14]	邹联沛1, 陈芳1, 王欣泽2, 孙瑞茹1, 宋召凤1. 生物绳-湿地植物复合人工湿地深度净化微污染水体的试验[J]. 上海大学学报(自然科学版), 2013, 19(5): 465-469.
[15]	张玲, 李梦雪, 周奇. 镧铁复合吸附剂的制备及除磷性能[J]. 上海大学学报(自然科学版), 2013, 19(4): 331-335.