Journal of Shanghai University(Natural Science Edition) ›› 2010, Vol. 16 ›› Issue (1): 35-37.
• Material Science • Previous Articles Next Articles
HOU Xue-ling1,2,HU Xing-hao2,WANG Xue-zhen2,ZENG Zhi2,XU Hui1,2,ZHOU Bang-xin1,2
Received:
Online:
Published:
Abstract:
[It was found in a study on the magnetocaloric effect of Gd5Si2-xGe2Znx and Gd5Si2-zGe2-zZn2z serial alloys that a trace amount of change of Zn element has a great impact on magnetocaloric properties of GdSiGeZn. The maximum isothermal magnetic entropy change (ΔSM) reaches 20.70 J/(kg·K) at 284 K and 25.30 J/(kg·K) at 280 K for x=0.001 and 2z=0.001. These magnetocaloric properties are better than that of undoped Gd5Si2Ge2 compound. Experimental results show Gd5Si2Ge2compound which are alloyed by a trace amount of Zn element has better magnetocaloric properties than that of Gd5Si2Ge2compound alloyed by other elements reported in the literature. The overall magnetocaloric properties are the best among other Gd5Si2Ge2alloys upon 5 T applied field.
Key words: magnetocaloric effect; isothermal magnetic entropy change; Curie temperature
CLC Number:
TF 125
HOU Xue-ling1,2,HU Xing-hao2,WANG Xue-zhen2,ZENG Zhi2,XU Hui1,2,ZHOU Bang-xin1,2. Magnetocaloric Effect of GdSiGeZn Compound under Applied Low Magnetic Field[J]. Journal of Shanghai University(Natural Science Edition), 2010, 16(1): 35-37.