Controllable synthesis of ZnO with different structures and its effect on gas sensitivity
Received date: 2020-02-06
Online published: 2021-05-10
材料的微观形貌是影响其气敏性能的主要因素. 低维结构材料因反应时的团聚问题, 极大地限制了其应用. 因此, 通过设计合成多级结构的纳米材料来提高性能至关重要. 通过控制水热时间、阴离子表面活性剂柠檬酸钠的浓度以及 pH 值来调节形貌, 在水热条件下成功合成了多级片球状、片花状以及馒头状 3 种形貌的 ZnO 纳米材料. 通过对气敏性能进行测试, 发现多级片球状形貌具有较好的气体敏感性. 在 340 ${^\circ}$C 时, 对 100$\times10^{-6}$ 正丁醇的气敏响应达到 238, 比相同条件下的乙醇高 2.12 倍, 显示出了较好的选择性. 通过研究多级结构的生长机理及传感机制, 为设计多级体系结构 ZnO 高性能气敏材料提供了数据依据.
李绅, 周荻雯, 何新华, 李飞, 宁珠凯, 焦正 . 不同结构 ZnO 的可控合成及其对气敏性能的影响[J]. 上海大学学报(自然科学版), 2022 , 28(2) : 304 -313 . DOI: 10.12066/j.issn.1007-2861.2285
The micromorphology of a material is the main factor that influencesits gas sensitivity. Applications of low-dimensional structuralmaterials are greatly limited because of agglomeration issues duringreactions. The performance of nanomaterials can be improved bydesigning and synthesising multilevel structures. Materialmorphology was mainly adjusted by controlling the hydrothermal time,the concentration of anionic surfactant citrate ions and hydroxideions. The ZnO nanomaterial synthesised under the controlledhydrothermal conditions had three types of morphologies,pompon-like, flaky-flower-shaped, and buns-like. The pompon-like ZnOshowed good gas sensitivity. At 340 $^\circ$C, itsgas-sensitive response to 100$\times10^{-6}$ n-butanol was 238,which was 2.12 times higher than that in case of ethanol, showinggood selectivity. In addition, by investigating the growth andsensing mechanisms of the multistage structure of ZnO, insights wereprovided for designing high-performance gas sensitive materialsusing multilevelarchitecture of ZnO.
Key words： multistage structure; ZnO; gas sensitivity
| [1] | Huang J, Yu K, Gu C, et al. Preparation of porous flower-shaped SnO$_{2}$ nanostructures and their gas-sensing property[J]. Sensors and Actuators B: Chemical, 2010, 147(2): 467-474. |
| [2] | Han B, Liu X, Xing X, et al. A high response butanol gas sensor based on ZnO hollow spheres[J]. Sensors and Actuators B: Chemical, 2016, 237: 423-430. |
| [3] | Yang P, Xiao X, Li Y, et al. Hydrogenated ZnO core-shell nanocables for flexible supercapacitors and self-powered systems[J]. ACS Nano, 2013, 7(3): 2617-2626. |
| [4] | Dong Z, Lai X, Halpert J E, et al. Accurate control of multishelled ZnO hollow microspheres for dye-sensitized solar cells with high efficiency[J]. Advanced Materials, 2012, 24(8): 1046-1049. |
| [5] | Zhao X, Li M, Lou X. Sol-gel assisted hydrothermal synthesis of ZnO microstructures: morphology control and photocatalytic activity[J]. Advanced Powder Technology, 2014, 25(1): 372-378. |
| [6] | Downing J M, Ryan M P, Mclachlan M A. Hydrothermal growth of ZnO nanorods: the role of KCl in controlling rod morphology[J]. Thin Solid Films, 2013, 539: 18-22. |
| [7] | Xiong H M. ZnO nanoparticles applied to bioimaging and drug delivery[J]. Advanced Materials, 2013, 25(37): 5329-5335. |
| [8] | Huang J, Wu Y, Gu C, et al. Large-scale synthesis of flowerlike ZnO nanostructure by a simple chemical solution route and its gas-sensing property[J]. Sensors and Actuators B: Chemical, 2010, 146(1): 206-212. |
| [9] | Li H, Wang X. Three-dimensional architectures constructed using two-dimensional nanosheets[J]. Science China Chemistry, 2015, 58(12): 1792-1799. |
| [10] | Sohila S, Rajendran R, Yaakob Z, et al. Photoelectrochemical water splitting performance of flower like ZnO nanostructures synthesized by a novel chemical method[J]. Journal of Materials Science: Materials in Electronics, 2015, 27(3): 2846-2851. |
| [11] | Cheng C L, Che P Y, Chen B Y, et al. High yield bio-butanol production by solvent-producing bacterial microflora[J]. Bioresource Technology, 2012, 113: 58-64. |
| [12] | Min B. SnO$_{2}$ thin film gas sensor fabricated by ion beam deposition[J]. Sensors and Actuators B: Chemical, 2004, 98(2/3): 239-246. |
| [13] | Korotcenkov G. Gas response control through structural and chemical modification of metal oxide films: state of the art and approaches[J]. Sensors and Actuators B: Chemical, 2005, 107 (1): 209-232. |
| [14] | Ma P, Wu Y, Fu Z, et al. Shape-controlled synthesis and photocatalytic properties of three-dimensional and porous zinc oxide[J]. Journal of Alloys and Compounds, 2011, 509(8): 3576-3581. |
| [15] | Guo W, Liu T, Zhang H, et al. Gas-sensing performance enhancement in ZnO nanostructures by hierarchical morphology[J]. Sensors and Actuators B: Chemical, 2012, 166: 492-499. |
| [16] | Liu C, Wang B, Liu T, et al. Facile synthesis and gas sensing properties of the flower-like NiO-decorated ZnO microstructures[J]. Sensors and Actuators B: Chemical, 2016, 235: 294-301. |
| [17] | Xiao Y, Lu L, Zhang A, et al. Highly enhanced acetone sensing performances of porous and single crystalline ZnO nanosheets: high percentage of exposed (100) facets working together with surface modification with Pd nanoparticles[J]. ACS Applied Materials & Interfaces, 2012, 4(8): 3797-3804. |
| [18] | Wang H, Wang C, Chen Q, et al. Interface-defect-mediated photocatalysis of mesocrystalline ZnO assembly synthesized in-situ via a template-free hydrothermal approach[J]. Applied Surface Science, 2017, 412: 517-528. |
| [19] | Guo W, Liu T, Zeng W, et al. Gas-sensing property improvement of ZnO by hierarchical flower-like architectures[J]. Materials Letters, 2011, 65(23/24): 3384-3387. |
| [20] | Roy S, Roy T K. Grain growth kinetics of Er$_{2}$O$_{3}$ doped ZnO-V$_{2}$O$_{5}$ based varistor ceramics[J]. Ceramics International, 2019, 45(18): 24835-24850. |
| [21] | Li F, Yang L, Xu G, et al. Hydrothermal self-assembly of hierarchical flower-like ZnO nanospheres with nanosheets and their application in Li-ion batteries[J]. Journal of Alloys and Compounds, 2013, 577: 663-668. |
| [22] | Neri G, Bonavita A, Micali G, et al. Resistive CO gas sensors based on In$_{2}$O$_{3}$ and InSnO$_{x}$ nanopowders synthesized via starch-aided sol-gel process for automotive applications[J]. Sensors and Actuators B: Chemical, 2008, 132(1): 224-233. |
| [23] | Kim H R, Choi K I, Kim K M, et al. Ultra-fast responding and recovering C$_{2}$H$_{5}$OH sensors using SnO$_{2}$ hollow spheres prepared and activated by Ni templates[J]. Chemical Communications, 2010, 46(28): 5061-5063. |
| [24] | An D, Wang Q, Tong X, et al. ZnO-enhanced In$_{2}$O$_{3}$-based sensors for n-butanol gas[J]. Ceramics International, 2019, 45(6): 6869-6874. |
| [25] | Kaneti Y V, Yue J, Jiang X, et al. Controllable synthesis of ZnO nanoflakes with exposed (1010) for enhanced gas sensing performance[J]. The Journal of Physical Chemistry C, 2013, 117(25): 13153-13162. |
| [26] | Zou T, Zhao R, Wang Z, et al. Sensitive and selective n-butanol gas detection based on ZnO nanocrystalline synthesized by a low-temperature solvothermal method[J]. Physica E: Low-dimensional Systems and Nanostructures, 2018, 103: 143-150. |
| [27] | Xu Y, Zheng L, Yang C, et al. Chemiresistive sensors based on core-shell ZnO @TiO$_{2}$ nanorods designed by atomic layer deposition for n-butanol detection[J]. Sensors and Actuators B: Chemical, 2020, 310: 127846. |
| [28] | Wei N, Cui H, Wang X, et al. Hierarchical assembly of In$_{2}$O$_{3}$ nanoparticles on ZnO hollow nanotubes using carbon fibers as templates: enhanced photocatalytic and gas-sensing properties[J]. Journal of Colloid and Interface Science, 2017, 498: 263-270. |
/
| 〈 |
|
〉 |